Carbide Square Bar Tungsten Carbide Customize

• Application: Aviation, Electronics, Industrial
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Purity: >99.99%
• Alloy: Alloy
• Shape: Round
• Type: Tungsten Bars
• Model NO.: Square bar
• Diameter: From 1mm to 35mm
• Length: From 50mm to 720mm
• Transport Package: Plastic Box
• Specification: From 1mm to 35mm Diameters. Any length
• Trademark: JXTC
• Origin: China
• Production Capacity: 1000tons/Year

Product Description

Mature and complete industrial chain from the very beginning of mining to control the quality, and customize professional materials.








Recommended Grade:

Grade	ISO application	grain size	Colbalt content	density g/cm³	hardness(HRA)	bending strength	Application
JT204N	K10-K20	0.2	9	14.4	94.0	3800	Super fine grain produced by H.C.Starck gives JT204N better bending resistance. JT204N is suitable for PCB micro-milling cutter, diameter of which is less than 0.4mm micro-milling cutter, as well as milling of high hard steel above 60HRC.
JT104U	K05-K10	0.4	6.5	14.72	94.0	3800	Fine grain produced by H.C.Starck gives JT104F better bending resistance. JT104F is suitable for PCB micro-milling cutter, diameter of which is less than 0.8mm micro-milling cutter.
JT104F	K05-K10	0.6	6	14.85	93.5	3500	Super fine grain produced by H.C.Starck and low cobalt content gives JT104F high hardness and better heat conductivity.Suitable for general aluminum semi-finishing and finishing processing.
JT404U	K30-K40	0.5	12	14.14	92.8	4200	Fine grain produced by H.C.Starck gives JT404U the combination of good wear-resistance and bending resistance. JT404U is suitable for universal processing of steel (below HRC45) .
JT304F	K20-K30	0.7	10	14.45	91.7	4000	Fine grain produced by H.C.Starck gives JT304F the combination of good wear-resistance and bending resistance. JT304F is suitable for universal processing of steel (below HRC45) .
JT304	K20-K30	0.8	10	14.45	91.5	3800	Fine grain produced by H.C.Starck gives JT304F the combination of good wear-resistance and bending resistance. JT304F is suitable for universal processing of steel (below HRC45) .
JT404F	K30-K40	0.6	11.5	14.14	92.8	4100	Fine grain produced by H.C.Starck gives JT404F the combination of good wear-resistance and bending resistance. JT404 is suitable for universal processing of steel ( HRC:45-55) .